UNS DesignationB | TypeB | Carbon | Manganese | Phosphorus | Sulfur | Silicon | Chromium | Nickel | Molybdenum | Nitrogen | Other Elements |
---|---|---|---|---|---|---|---|---|---|---|---|
Precipitation Hardening Grades | |||||||||||
S17400 | 630 | 0.07 | 1.00 | 0.040 | 0.030 | 1.00 | 15.0-17.0 | 3.0-5.0 | ... | ... | Cu 3.0-5.0, |
A. Maximum or range unless otherwise indicated.
B. See Guide A959/A959M.
Samples taken from product (see the section in Specification A962/A962M titled “Mechanical Properties”) shall conform to the mechanical properties of Tables 2-4.
Age hardened bolting material shall be capable of meeting the requirements prescribed in Table 3. Impact testing is required when S1 is invoked in the purchase order or contract.
Number of Tests:
Bolting Material— See 8.4 for hardness testing of bar.
See the section in Specification A962/A962M
titled “Number of Tests” for all other tests except those covered in 8.3.2.
Full Size Bolting Components— Headed bolts with a 1 1 ⁄ 2 in. [37 mm] body diameter and
smaller, with a body length three times the diameter or longer and a required maximum
tensile load of 160 000 lb/f [705 kN], produced by upsetting or
forging (hot or cold) shall be subjected to full size testing. The
testing shall be in addition to the tensile testing specified in above Bolting Point.
The lot size shall be as shown in Specification
A962/A962M
(see the section titled Number of Tests). Failure shall
occur in the body or threaded section with no failure, or
indications of failure, such as cracks, at the junction of the head
and shank. Wedge tensile testing is not required for flat
countersunk head or socket button products.
Hardness Test:
Bolting Material Bars 2 in. [50 mm] and Over— One
test on each mill-treated length.
Bolting Material Bars Under 2 in. [50 mm]— One test
on at least 10 % of the mill treated lengths.
UNS Designation | Type | Solution TreatmentB,C °F [°C] | Mechanical Property Requirements in the Solution Treated Condition | |||||
---|---|---|---|---|---|---|---|---|
Tensile Strength ksi [MPa] | Yield Strength ksi [MPa] | Elongation in 2” [50 mm] or 4D, min. % | Reduction of Area, min. % | HardnessD | ||||
Rockwell, maximum | Brinell, maximum | |||||||
S17400 | 630 | Cool to below 90 [32] | ... | ... | ... | ... | 38 HRC | 363 |
A. Values shown are minimums or ranges unless maximum is indicated.
B. 1900 [1040] ± 25°F [15°C].
C. Quenched in water unless the table specifies another media.
D. Either Rockwell or Brinell testing is permitted unless thickness is below 1⁄2 ” in which
case Rockwell is preferred.
UNS Designation | Type | Condition | Grade Symbol |
---|---|---|---|
Duplex (Ferritic-Austenitic) Grade | |||
S17400 | 630 | -- | 174 |
S17400 | 630 | H900 | 174A |
S17400 | 630 | H925 | 174B |
S17400 | 630 | H1025 | 174C |
S17400 | 630 | H1075 | 174D |
S17400 | 630 | H1100 | 174E |
S17400 | 630 | H1150 | 174G |
S17400 | 630 | H1150D | 174H |
S17400 | 630 | H1150M | 174J |